Pioneers in the industry, we offer syndino products, syndino top and syndino ring from India.
Approx. Price: Rs 2,050 / KgGet Latest Price Lawatherm is manufacturing syndino products in various size and shapes of sheet, rod, spacer, segment, half round syndino turn, top & bottom. These sheets are available in various sizes from 2mm to 75mm.
CompositionLawatherm consist of asbestos fiber and cement formed into fully compressed boards under high pressure, mechanically strong, these boards possess good arc and heat resisting characteristics are used for thermal insulation as well aselectrical insulation.
Application- Insulation of high temperature heated platens and moulds in hydraulic and presses
- High temperature insulation of electrode arm in arc furnaces and ladle furnaces
- High temperature insulation between coil and crucible in induction furnaces
- Insulation in dynamic braking resistors used in locomotives
- Applications requiring high voltage resistance at high temperatures
| Specification | Requirement As per IS:4248 | Sindhanio 450 Obtained Value |
| Continuous Operating Temperature |
| 450 °C (Max) |
| Density (Kg/m3) |
| 1900 |
| Thermal Conductivity (W/m OK) |
| 0.64 |
| Cross-breaking strength (Kg/cm2) | Min. 300 | 366 |
| Crushing Strength (Kg/cm2) | Min. 1055 | 1536 |
| Shear Strength (Kg/cm2) | Min. 210 | 437 |
| Deformation under Compression, Kgf | Reduction in | Reduction in |
| thickness shall | thickness: 2 % | |
| not be greater |
|
| than 5% nor |
|
Approx. Price: Rs 2,050 / KgGet Latest Price Lawatherm is manufacturing syndino products in various size and shapes of sheet, rod, spacer, segment, half round syndino turn, top & bottom. These sheets are available in various sizes from 2mm to 75mm.
CompositionLawatherm consist of asbestos fiber and cement formed into fully compressed boards under high pressure, mechanically strong, these boards possess good arc and heat resisting characteristics are used for thermal insulation as well aselectrical insulation.
Application- Insulation of high temperature heated platens and moulds in hydraulic and presses
- High temperature insulation of electrode arm in arc furnaces and ladle furnaces
- High temperature insulation between coil and crucible in induction furnaces
- Insulation in dynamic braking resistors used in locomotives
- Applications requiring high voltage resistance at high temperatures
| Specification | Requirement As per IS:4248 | Sindhanio 450 Obtained Value |
| Continuous Operating Temperature | | 450 °C (Max) |
| Density (Kg/m3) | | 1900 |
| Thermal Conductivity (W/m OK) | | 0.64 |
| Cross-breaking strength (Kg/cm2) | Min. 300 | 366 |
| Crushing Strength (Kg/cm2) | Min. 1055 | 1536 |
| Shear Strength (Kg/cm2) | Min. 210 | 437 |
| Deformation under Compression, Kgf | Reduction in | Reduction in |
| thickness shall | thickness: 2 % | |
| not be greater | |
| than 5% nor | |
Approx. Price: Rs 2,050 / KgGet Latest Price Lawatherm is manufacturing syndino products in various size and shapes of sheet, rod, spacer, segment, half round syndino turn, top & bottom. These sheets are available in various sizes from 2mm to 75mm.
CompositionLawatherm consist of asbestos fiber and cement formed into fully compressed boards under high pressure, mechanically strong, these boards possess good arc and heat resisting characteristics are used for thermal insulation as well aselectrical insulation.
Application- Insulation of high temperature heated platens and moulds in hydraulic and presses
- High temperature insulation of electrode arm in arc furnaces and ladle furnaces
- High temperature insulation between coil and crucible in induction furnaces
- Insulation in dynamic braking resistors used in locomotives
- Applications requiring high voltage resistance at high temperatures
| Specification | Requirement As per IS:4248 | Sindhanio 450 Obtained Value |
| Continuous Operating Temperature | | 450 °C (Max) |
| Density (Kg/m3) | | 1900 |
| Thermal Conductivity (W/m OK) | | 0.64 |
| Cross-breaking strength (Kg/cm2) | Min. 300 | 366 |
| Crushing Strength (Kg/cm2) | Min. 1055 | 1536 |
| Shear Strength (Kg/cm2) | Min. 210 | 437 |
| Deformation under Compression, Kgf | Reduction in | Reduction in |
| thickness shall | thickness: 2 % | |
| not be greater | |
| than 5% nor | |